Quality printing material brand Fiber3D .
Material with wood admixture for better product appearance. Your prints get the look of wooden products. This is a material suitable for use in 3D printers. It is very firm, does not exclude chemical odor, biodegradable (made of renewable natural resources) during printing. Wood material can be easier to print large parts.
Material description: PLA, Polylactic acid, Polymonic acid is bioplastic produced from corn starch. The properties are similar to the plastic, which are made of oil. Wood is more gentle on nature than ABS. It is a material that can be dissolved in tetrahydrofuren. Long -term exposure to acetone may be etched. PLA is not healthy and is degradable in nature (controlled composting). Compared to ABS, the strength of the material is higher, the material is better printable. Wood can be actively cooling during printing and also does not need a heated pad. The disadvantages of the material are lower temperature resistance, greater abrasiveness to the output nozzle and very often necessary slower printing speed.
The Pla Wood processing temperature is 190 - 220 ° C.
PLA: The material cannot be easily modified as the heat is produced that causes "pulling" fibers from the print. It is therefore advisable to cool the print, for example, to grind it underwater. Similarly, when drilling holes into prints. It is advisable to spray the material first (used in modeling) and then grind, spray and repeat until you think the surface is perfectly smooth. In conclusion, the print can be sprayed with paint. The resulting model can also be inserted into the "tissue" along with shells, stones, remnants of filaments, pieces of prints.
Storage: We recommend securing a dry environment. In poor storage in a humid environment, it absorbs moisture, which manifests itself as bubbles on the surface. Protect from heat.
Main advantages of PLA:
- small shrinking when cooling-not a necessary heated pad or chamber
- good print quality even when printing at high speed
- soluble in sodium hydroxide
- biologically degradable material
Supplied in color wood.
10 meter sample (+-1 meter-packed manually)
Warning: samples are intended for immediate use.
More from category
Additional information
Category: | Samples, swatches |
Color: | wood |
Weight: | vzorek |
Average: | 1,75 mm |
Diameter: | ± 0,02 mm |
Bed temperature: | 0-60° C |
Nozzle temperature: | 190 - 220° C |